Adsorbent activity characterization

ABSTRACT

The present invention is directed to a method of determining the degree of saturation of a decontamination-removing substance or adsorbent such as an alumina absorbent or activated charcoal. The method is sufficiently sensitive to detect changes in the bulk specific electrical conductivity of the adsorbent.

FIELD OF THE INVENTION

[0001] The present invention is directed to a method of determining the degree of saturation of an adsorbent material. More particularly, it is directed to measuring changes in conductivity to establish a change in adsorptive capacity.

BACKGROUND OF THE INVENTION

[0002] In many industrial processes the moisture content of gaseous streams should be reduced to a very low level, to prevent corrosion (production of dodecylbenzylsulfonic acid used in detergent industry) and/or side reactions (hydrolysis of reactants). Fixed bed dryers are generally used where the moisture content of the gases is reduced by adsorption/absorption on solid absorbents. Water molecules are entrapped in the capillaries on the particle surface. Depending on the type of the adsorbent, unwanted side products might form. In order to avoid the formation of such byproducts, some absorbents must be pretreated. After the pretreatment the adsorbent is used on-stream until completely saturated. The saturated absorbent is usually regenerated by desorbing water to be used again for drying. The saturation-drying cycle is repeated many times. A regeneration factor can be defined which shows what percentage of the absorbed water can be removed and what capacity will be available for the next cycle.

%regeneration factor=The amount of desorbed moisture/Total amount of absorbed water (completely saturated)×100

[0003] 100% regeneration factor means complete removal of the absorbed water.

[0004] Other adsorbents such as activated charcoal are used to adsorb hydrocarbon fumes. The activity of the adsorbent gradually decreases as it becomes saturated by hydrocarbons. The spent adsorbent must then be replaced or regenerated. The present invention is directed to a method for determining the relative capacity/activity of activated charcoal based on conductivity measurements.

[0005] Conductivity measurements in the solid phase are relatively easy and are used to characterize materials containing ionic species. For instance, the electrical conductivity of pure and doped Fe₂O₃, and the effect of gamma-irradiation on the electrical conductivity was studied (M. A. Mousa, E. A. Gomaa, A. A. El-Khouly and A. A. M. Aly: Mater. Chem. Phys. 11, 433 (1984)). Doping either increased or decreased the electrical conductivity of pure Fe₂O₃(σ*=1.5×10⁻⁶ [Ω⁻¹ cm⁻¹]), depending on the type and amount of doping elements. Gamma-irradiation increased the conductivity of pure Fe₂O₃, which in turn decreased upon annealing. Higher doses caused higher conductivity increases, which was explained by increasing charge carrier (Fe²⁺) concentrations. The above mentioned paper investigated these oxides in terms of semiconducting properties.

[0006] Soviet Union Patent No. 1221571 discusses monitoring of the decomposition of peroxides using a semiconductor sensor. Free electrons forming during the decomposition of the peroxides affect the electrical properties of the sensor. This differs fundamentally from the present invention in which ionic compounds are involved.

[0007] Japanese Patent No. HEI 1-253645 discloses a tube type of bed in which electrodes are placed at the entrance and exit of the tube. In this circuit, the bed represents a certain resistance which is greater than the resistance of the carbon due to voids between particles. When a solvent saturates the bed and fills the cavities, the resistance of the bed decreases. This is essentially the same as shorting out a circuit by moisture; the vapor/liquid provides an alternative conducting route. It is clearly apparent that this method is only useful for measuring gross changes in conductivity.

[0008] The present disclosure is directed to a method of measuring changes in conductivity as an indicator of relative adsorbent activity of an absorptive substance, such as an alumina absorbent or a decontaminating substance such as activated charcoal. Resistance is measured on a single bead or in a packed bed. As the degree of adsorption increases, the route of electrons is blocked and the resistance increases. The method of the current invention is capable of detecting changes in conductivity orders of magnitude smaller than the changes detectable by the Japanese method. The high level of sensitivity of the present invention ensures that the degree of saturation can be monitored to ensure that absolutely no break-through occurs. This is essential in industrial applications where the degree of saturation is rarely allowed to exceed 20%. Conductivity measurements are determined in the adsorptive phase. The adsorptive phase is defined as the stage at which all the sorbant is held to the sorptive material by physical or chemical means. Thus, for the present invention, in contrast to the above mentioned Japanese patent, as soon as molecules are in free phase, the adsorptive material is already saturated.

SUMMARY OF THE INVENTION

[0009] The present invention is directed to a method of monitoring the relative capacity of adsorbents at various stages of saturation by measuring an electrical property of the adsorbent and correlating a value for conductivity to adsorptive capacity. Changes in conductivity are determined during the adsorptive phase in which the material to be adsorbed is bound to the adsorptive material by physical or chemical means.

BRIEF DESCRIPTION OF THE DRAWINGS

[0010] The invention is described in more detail herein with reference to the accompanying drawings, in which:

[0011]FIG. 1 illustrates a comparison of the conductivities of pretreated and saturated alumina adsorbent;

[0012]FIGS. 2A and 2B illustrate a comparison of the conductivities of fresh and used active carbon for a packed bed and a single bead;

[0013]FIG. 3 illustrates the effect on conductivity when CO₂ is adsorbed to activated carbon;

[0014]FIG. 4 illustrates a comparison of the conductivities of regenerated and saturated molecular sieve in a packed bed configuration; and

[0015]FIG. 5 illustrates a comparison of regenerated and saturated molecular sieve on a single bead.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0016] The present invention is concerned with easy monitoring methods to follow and interpret the electrical properties, such as specific conductivity or resistance, of various adsorbent materials. The data disclosed herein and detailed in the examples below demonstrate that conductivity measurements are a reliable indicator of the degree of exhaustion of the adsorbent materials, such alumina absorbents and activated charcoal. The novel method is sensitive enough to detect minute changes in the bulk specific electrical conductivity of the adsorbents.

[0017] One method for determining an electrical property of the adsorbent which relates to conductivity, measures the d.c. resistance of a single bead while another method measures the d.c. resistance of a packed bed between two parallel plates. The resistance was either measured directly or by measuring the voltage drop across the catalyst (single bead or packed bed).

[0018] The following abbreviations will be used to describe the various methods:

[0019] RS=direct resistance measurement, single bead

[0020] RP=direct resistance measurement, packed bed

[0021] VS=voltage drop measurement, single bead

[0022] VP=voltage drop measurement, packed bed

[0023] The resistance is obtained from calibration curves constructed by using known resistors as R_(X), to account for the internal impedance of the electrometer (Keithley Model 600 B).

[0024] The direct resistance measurement and the voltage drop measurement yield identical values within experimental error as expected. The resistance in a packed bed is a combination of the resistance of the beads and the voids (in this case air). The specific conductivity σ*[Scm⁻¹ or Ω⁻¹ cm⁻¹] is calculated from equation 1:

R=Ω*L/A  [1]

[0025] where L and A are the length and the cross section of the resistor in cm and cm², respectively. In case of a single bead average bead dimensions are used; in case of the packed bed L is the distance of the parallel plates (L=1.2 cm) and A is the surface of the electrodes immersed in the bed (Λ=4 cm²).

[0026] Conductivity measurements do not differentiate between conductive species, but from the practical point of view it is enough to pinpoint a change signaling saturation. As sorbant binds to an adsorptive material, the conductivity may increase or decrease. The direction of the change depends upon the innate resitivity of the starting material and the relative conductivities of the adsorptive material and the sorb ant. We have found the surprising result that conductivity does change during the adsorptive phase and that changes can be detected when the level of saturation of the adsorptive material is low, typically less than 20% saturated. This surprising result is further demonstrated in the following examples.

[0027] Alumina adsorbents were tested by the method of the present invention. The results discussed in Examples 1 through 14 demonstrate that the conductivity changes correlate with the capacity of alumina adsorbents. Activated charcoal used for adsorbing hydrocarbon fumes was also tested by the present invention and the results are discussed in Example 15. Experiments were also conducted to evaluate the use of the method to determine adsorption of carbon dioxide and to determine its applicability to molecular sieve technology.

EXAMPLES

[0028] The above disclosure generally describes the invention. A more complete understanding can be obtained by reference to the following specific examples. These examples are described solely for purposes of illustration and are not intended to limit the scope of the invention.

Example 1

[0029] A commercial pretreated alumina adsorbent (AL12) was investigated. The conductivity of the pretreated adsorbent was RS−8.17×10⁻⁹ and VS=8.09×10⁻⁹ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated adsorbent was measured to be two orders of magnitude higher than that of the pretreated adsorbent—RS=6.85×10⁻⁷; VS=6.45×10⁻⁷ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 7.62×10⁻⁹ [Ω⁻¹ cm⁻¹]. The results are summarized in Table I below. TABLE I Pretreated, Saturated, Test # (Ω-cm)⁻¹ × 10⁹ (Ω-cm)⁻¹ × 10⁷ 1 3.47 1.67 2 9.62 3.13 3 7.58 0.96 4 20.83 2.08 5 9.62 2.78 6 5.56 11.90 7 4.90 8.62 8 6.94 13.89 9 3.42 8.06 10  52.08 1.39 STDEV 14.82 4.77 Average 8.09 6.45

[0030]FIG. 1 illustrates graphically a comparison between the pretreated and saturated samples. The regeneration cycle was repeated three times for this sample and nearly complete regeneration was observed as shown below in Table II.

[0031] The large difference between the conductivities of unsaturated and saturated adsorbent demonstrate the feasibility of the method of the present invention for indicating exhaustion.

Example 2

[0032] A commercial pretreated alumina adsorbent, AL13 was investigated. The conductivity of the pretreated adsorbent was RS=5.57×10⁻⁹ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated adsorbent was measured to be two orders of magnitude higher than that of the pretreated adsorbent—RS=3.76×10⁻⁷ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the cycle was repeated three times for this sample and nearly complete regeneration was observed as shown in Table II for sample AL13. TABLE II Regeneration data of alumina gel samples Sample Regeneration Code/No. First factor Third Conductivity Description Regen. Second Regen. Regen. (Ω-cm)⁻¹ AL12 98.7 98.4 98.6 7.62E-9  AL13 99.5 98.6 98.3 5.54E-9  AL14 99.3 99.5 98.4 8.18E-9  AL15 98.2 98.8 97.9 1.42E-12

Example 3

[0033] A commercial pretreated alumina adsorbent, AL14 was investigated. The conductivity of the pretreated adsorbent was RS=9.46×10⁻⁹ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated adsorbent was measured to be two orders of magnitude higher than that of the pretreated adsorbent—RS=8.61×10⁻⁷ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 8.18×10⁻⁹ [Ω⁻¹ cm⁻¹]. The regeneration cycle was repeated three times for this sample and nearly complete regeneration was observed as shown above in Table II.

Example 4

[0034] A commercial alumina adsorbent (AL15) was investigated. The conductivity of the unused adsorbent was RS=3.75×10⁻¹² [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated adsorbent was measured to be two orders of magnitude higher than that of the unused absorbent—RS=1.47×10⁻¹⁰ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 1.42×10⁻¹² [Ω⁻¹ cm⁻¹] as shown in Table II.

Example 5

[0035] A commercial alumina (AL2) absorbent was investigated. The conductivity of the unused absorbent was RS=7.60×10⁻¹² [Ω⁻¹ cm⁻¹ ] on a single bead. The conductivity of the saturated absorbent was measured to be two orders of magnitude higher than that of the unused absorbent—RS=5.63×10⁻¹⁰ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 1.86×10⁻¹² [Ω⁻¹ cm⁻¹]. The regeneration cycle was repeated three times for this sample and nearly complete regeneration was observed.

Example 6

[0036] A commercial alumina (AL3) absorbent was investigated. The conductivity of the unused absorbent was RS=5.26×10⁻¹¹ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated absorbent was measured to be two orders of magnitude higher than that of the unused absorbent—RS =7.83×10⁻⁹ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 5.65×10⁻¹¹ [Ω⁻¹ cm⁻ ¹].

Example 7

[0037] A commercial alumina (AL4) absorbent was investigated. The conductivity of the unused absorbent was RS=7.91×10⁻¹¹ [Ω⁻¹ cm⁻ ¹ ] on a single bead. The conductivity of the saturated absorbent was measured to be two orders of magnitude higher than that of the unused absorbent—RS =8.65×10⁻⁹ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 3.67×10⁻¹¹ [Ω⁻¹ cm⁻¹].

Example 8

[0038] A commercial alumina (AL5) absorbent was investigated. The conductivity of the unused absorbent was RS=8.70×10⁻¹¹ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated absorbent was measured to be two orders of magnitude higher than that of the unused absorbent—RS=2.28×10⁻¹⁰ [Ω⁻¹ cm⁻ ¹]. This sample was regenerated, and the conductivity of the regenerated sample was 3.85×10⁻¹¹ [Ω⁻¹ cm⁻¹].

Example 9

[0039] A commercial alumina (AL6) absorbent was investigated. The conductivity of the unused absorbent was RS=6.06×10⁻¹¹ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated absorbent was measured to be two orders of magnitude higher than that of the unused absorbent—RS=8.58×10⁻⁹ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 4.48×10⁻¹¹ [Ω⁻¹ cm⁻¹].

Example 10

[0040] A commercial alumina (AL7) absorbent was investigated. The conductivity of the unused absorbent was RS=4.24×10⁻¹¹ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated absorbent was measured to be two orders of magnitude higher than that of the unused absorbent—RS=8.61×10⁻⁹ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 4.13×10⁻¹¹ [Ω⁻¹ cm⁻¹].

Example 11

[0041] A commercial alumina (AL8) absorbent was investigated. The conductivity of the unused absorbent was RS=1.65×10⁻⁹ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated absorbent was measured to be two orders of magnitude higher than that of the unused absorbent—RS=6.44×10⁻⁷ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 1.72×10⁻⁹ [Ω⁻¹ cm⁻¹].

Example 12

[0042] A commercial pretreated alumina (AL9) absorbent was investigated. The conductivity of the pretreated absorbent was RS=3.04×10⁻⁹ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated absorbent was measured to be close to that of the pretreated absorbent—RS=1.05×10⁻⁹ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 2.68×10⁻⁹ [Ω⁻¹ cm⁻¹]. This sample appeared to be totally exhausted.

Example 13

[0043] A commercial pretreated alumina (AL10) absorbent was investigated. The conductivity of the pretreated absorbent was RS=1.56×10⁻¹⁰ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated absorbent was measured to be two orders of magnitude higher than that of the pretreated absorbent—RS=3.48×10⁻⁸ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 2.24×10⁻¹¹ [Ω⁻¹ cm⁻¹]

Example 14

[0044] A commercial pretreated alumina (AL 11) absorbent was investigated. The conductivity of the pretreated absorbent was RS=9.52×10⁻¹¹ [Ω⁻¹ cm⁻¹] on a single bead. The conductivity of the saturated absorbent was measured to be two orders of magnitude higher than that of the pretreated absorbent—RS=7.12×10⁻⁹ [Ω⁻¹ cm⁻¹]. This sample was regenerated, and the conductivity of the regenerated sample was 9.13×10⁻¹¹ [Ω⁻¹ cm⁻¹]. The results of all 14 samples are summarized in Tables II and III. TABLE III Results of alumina absorbent samples Electrical Conductivity Conductivity Sample Unsaturated Saturated Regeneration after Regen. Code/No. (Ω-cm)⁻¹ (Ω-cm)⁻¹ factor (Ω-cm)⁻¹ AL2 7.60E-12 5.63E-10 98.2 1.86E-12 AL3 5.26E-11 7.83E-9  92.7 5.65E-11 AL4 7.91E-11 8.65E-9  98.5 3.67E-11 AL5 8.70E-11 2.28E-10 93.4 3.85E-11 AL6 6.06E-11 8.58E-9  97.9 4.48E-11 AL7 4.42E-11 8.61E-9  88.5 4.13E-11 AL8 1.65E-9  6.44E-7  92.6 1.72E-9  AL9 3.04E-9  1.05E-9  — 2.68E-9  AL10 1.56E-10 3.49E-8  96.6 2.24E-9  AL11 9.52E-11 7.12E-9  98.2 9.13E-11 AL12 8.17E-9  6.85E-7  98.7 7.62E-9  AL13 5.57E-9  3.76E-7  99.5 5.54E-9  AL14 9.46E-9  8.61E-7  99.3 8.18E-9  AL15 3.75E-12 1.47E-10 95.6 1.42E-12

Example 15

[0045] Activated charcoal (Fluka, EC 2311533) used for the adsorption of hydrocarbon fumes was investigated. The conductivity of the fresh charcoal was RS=1.78×10⁻¹ and VS=1.72×10⁻¹ [Ω⁻¹ cm⁻¹] on a single cylindrical bead(L=0.61 cm; A=0.14 cm²), and RP=6.61×10⁻³ and VP=6.21×1⁻³ [Ω⁻¹ cm⁻¹] in a packed bed. The conductivity of the hydrocarbon-saturated charcoal was measured to be less than half of that of the fresh one—RS=8.16×10⁻²; VS=8.55×10⁻², RP=3.02×10⁻³ and VP=3.04×10⁻³ [Ω⁻¹ cm⁻¹]. The data are summarized in Tables IVa and IVb, and the comparison is shown graphically in FIG. 2. Thus this method can be a sensitive measure of the exhaustion of activated charcoal adsorbent beds used frequently in the chemical industry. TABLE Iva Conductivity Data of Active Carbon Single Bead Fresh Used Test # [Ω-cm]⁻¹ × 10⁻¹ [Ω-cm]⁻¹ × 10⁻² 1 2.22 9.50 2 1.47 9.65 3 1.85 7.45 4 2.39 9.14 5 2.13 7.69 6 1.22 8.00 7 1.62 7.61 8 1.45 7.32 9 1.27 10.18  10  1.60 8.92 STDEV 0.41 1.05 Average 1.72 8.55

[0046] TABLE IVb Packed Bed Fresh Used Test # [Ω-cm]⁻¹ × 10⁻³ [Ω-cm]⁻¹ × 10⁻³ 1 6.74 3.10 2 6.61 2.90 3 6.38 2.98 4 5.31 3.12 5 5.70 3.21 6 6.90 3.07 7 6.20 2.89 8 6.48 2.87 9 6.37 3.05 10  5.43 3.16 STDEV 0.55 0.12 Average 6.21 3.04

Example 16

[0047] The adsorption of carbon dioxide on activated charcoal was investigated. The conductivity of the fresh activated carbon was RS=1.72×10⁻² [Ω⁻¹ cm⁻¹]. The conductivity of the used adsorbent was 5.18×10⁻³ [Ω⁻¹ cm⁻¹]. The results are shown below in Table V and are illustrated graphically in FIG. 3. TABLE V Conductivity Data for the adsorption of CO₂ on Activated Carbon Method RS Fresh Used Test # [Ω-cm]⁻¹ × 10⁻² [Ω-cm]⁻¹ × 10⁻³ 1 1.69 5.04 2 1.80 5.19 3 1.74 5.28 4 1.69 5.25 5 1.65 5.21 6 1.78 5.20 7 1.71 5.13 8 1.76 5.07 9 1.69 5.22 10  1.72 5.23 STDEV 0.05 0.08 Average 1.72 5.18

Example 17

[0048] The adsorption of water on a molecular sieve was investigated. In a packed bed, the conductivity of the fresh sieve was 1.25×10⁻¹⁴ [Ω⁻¹ cm⁻¹] and the conductivity of the used adsorbent was 1.72×10⁻¹³ [Ω⁻¹ cm⁻¹]. The conductivity of the fresh adsorbent was 2.14×10⁻⁹ [Ω⁻¹ cm⁻¹] on a single bead while the used adsorbent had a conductivity of 2.01×10⁻¹⁰ [Ω⁻¹ cm⁻¹]. The results are shown in Tables Via and VIb below and are illustrated graphically in FIGS. 4 and 5. TABLE VIa Molecular Sieve Conductivity Data Method VP (Packed Bed) Fresh Used Test # [Ω-cm]⁻¹ × 10⁻¹⁴ [Ω-cm]⁻¹ × 10⁻¹³ 1 1.32 1.67 2 1.19 2.86 3 1.43 1.47 4 1.47 1.92 5 1.18 1.72 6 1.16 1.61 7 1.28 1.54 8 1.23 1.69 9 1.14 1.67 10  1.19 1.63 STDEV  0.115  0.914 Average 1.25 1.72

[0049] TABLE VIb Molecular Sieve Conductivity Data Method RS (Single Bead) Fresh Used Test # [Ω-cm]⁻¹ × 10⁻⁹ [Ω-cm]⁻¹ × 10⁻¹⁰ 1 6.25 2.38 2 5.00 3.57 3 3.33 1.52 4 1.00 1.06 5 1.54 0.50 6 2.00 1.00 7 0.63 1052 8 0.59 5.56 9 0.71 1.54 10  0.35 2.04 STDEV 2.06 1.49 Average 2.14 2.07

[0050] Although preferred embodiments of the invention have been described herein in detail, it will be understood by those skilled in the art that variations may be made thereto without departing from the spirit of the invention or the scope of the appended claims. 

1. A method for evaluating adsorptive capacity of an adsorptive material for a sorbant comprising monitoring electrical conductivity of said adsorptive material when said sorbant material is held on said adsorptive material by physical or chemical means.
 2. A method of claim 1 wherein said step of monitoring conductivity of said adsorptive material comprises measuring an electrical property of said adsorptive material which relates to said electrical conductivity.
 3. A method of claim 2 wherein said measured electrical property is resistivity and correlating measured resistivity with adsorptive capacity.
 4. A method of claim 2, wherein said measured electrical property is capacitance and correlating measured capacitance with adsorptive capacity.
 5. A method of claim 1 wherein said electrical conductivity of said adsorptive material is monitored over time to determine a change in electrical conductivity of said material, correlating a change in conductivity with a decrease in adsorptive capacity and correlating an opposite change in conductivity with an increase in adsorptive capacity.
 6. A method of claim 5 wherein a determined extent of decrease in conductivity correlates with said adsorptive material being saturated.
 7. A method of claim 5 wherein a determined extent of increase in conductivity correlates with said adsorptive material being regenerated.
 8. A method of claim 2 wherein said electrical property is measured on a single particle of adsorptive material.
 9. A method of claim 2 wherein said electrical property is measured “in situ” of a bed of adsorptive material in a treatment unit.
 10. A method of claim 2 wherein said electrical property is measured “in situ” of a bed of adsorptive material in a regenerator unit.
 11. A method of claim 9 wherein said electrical property is measured between two spaced apart electrodes positioned in a bed of said adsorptive material.
 12. A method of claim 10 wherein said electrical property is measured between two spaced apart electrodes positioned in a bed of said adsorptive material.
 13. A method of claim 1 wherein said adsorptive material is selected from the group consisting of activated carbon, alumina adsorbents and molecular sieve.
 14. A method of claim 13 wherein said adsorptive material is activated carbon.
 15. A method of claim 13 wherein said adsorptive material is aluminum oxide.
 16. An apparatus for assessing electrical conductivity of an adsorptive material to determine capacity of said material, said apparatus comprising: i) means for monitoring electrical conductivity of adsorptive material; and ii) means for correlating monitored conductivity with adsorptive material capacity.
 17. An apparatus of claim 16 wherein said monitoring means comprises spaced apart electrodes in contact with a particulate adsorptive material.
 18. An apparatus of claim 16 wherein means retains an adsorptive particle between said electrodes.
 19. An apparatus of claim 18 wherein said retaining means biases said electrodes against a adsorptive particle.
 20. An apparatus of claim 17 wherein said spaced apart electrodes are adapted to be placed in a bed of particulate adsorptive material to measure conductivity thereof.
 21. An apparatus of claim 16 wherein said correlating means for generating adsorptive capacity information based on monitored value for conductivity.
 22. An apparatus of claim 21 wherein said monitoring means determines at any point in time a value for electrical conductivity and said capacity information generating means providing a corresponding value for adsorptive capacity.
 23. An apparatus of claim 21 wherein said monitoring means monitors electrical conductivity over time to determine a change in electrical conductivity of said adsorptive material, said capacity information generating means correlating a change in conductivity with a decrease in adsorptive capacity and correlating an opposite change in conductivity with an increase in adsorptive capacity.
 24. An apparatus of claim 23 wherein said capacity information generating means is programmed to correlate a determined extent of increase in conductivity with a adsorptive material being saturated, said adsorptive material being aluminum oxide.
 25. An apparatus of claim 23 wherein said capacity information generating means is programmed to correlate a determined extent of decrease in conductivity with adsorptive material being saturated, said adsorptive material being activated carbon.
 26. A adsorptive tower having an apparatus of claim 16 for monitoring adsorptive capacity in said tower.
 27. A adsorptive material regenerator having an apparatus of claim 16 for monitoring adsorptive material capacity during an adsorptive regeneration cycle.
 28. A processor for correlating adsorptive capacity with measured electrical conductivity of a adsorptive material comprising: i) means for receiving a signal representative of surface electrical conductivity, and ii) programmable means for generating adsorptive capacity information based on monitored value for conductivity.
 29. A processor of claim 28 wherein said programmable means is programmed with a custom program for correlating conductivity with adsorptive capacity. 